Effect of laser irradiation on activation energy, irreversibility field and upper critical magnetic field of bulk MgB2 superconductor
In this study, the role of laser irradiation on the upper critical field (Hc2), the irreversibility field (Hirr) and the activation energy (U0) of bulk MgB2 superconductor was first time investigated with the aid of magnetoresistivity measurements conducted at different applied magnetic fields in a range of 0–15 kOe as a function of temperature from 25 to 40 K. For this aim, a disk shaped MgB2 superconductor was produced and cut into two pieces. One of the pieces was irradiated under high vacuum conditions by using an Nd:YVO4 laser. The obtained results showed an increase in the critical temperature (Tc) by about 1 K after irradiation. Also, the values of Hc2(0) were respectively found to be around 143 and 151 kOe while the values of Hirr(0) were about 122 and 130 kOe for the reference and the irradiated samples. Using the thermally activated flux flow model the dependence of U0 on magnetic field was determined. The maximum U0 values of 0.43 and 0.83 eV in zero magnetic field were respectively obtained for the reference and the irradiated samples. Also, the magnetic field dependence of the critical current density Jc(B) values at different temperatures were slightly increased after the irradiation. These results point out that the superconducting properties of bulk MgB2 can be improved via laser irradiation. © 2016, Springer Science+Business Media New York.
KaynakJournal of Materials Science: Materials in Electronics
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
This study reports the effect of coronene (C24H12) addition on some superconducting properties such as critical temperature (Tc), critical current density (Jc), flux pinning force density (Fp), irreversibility field (Hirr), ...
The effect of magnetic field distribution and pole array on the vertical levitation force properties of HTS Maglev systems Ozturk K.; Abdioglu M.; Sahin E.; Celik S.; Gedikli H.; Savaskan B. (Institute of Electrical and Electronics Engineers Inc., 2015)In this paper, the levitation force measurements have been carried out by the magnetic force measurement system under both field-cooling and zero-field-cooling regimes, whereas the magnetic field distribution over the ...
Effect of laser irradiation on superconducting properties of bulk MgB2 sintered at different temperatures The surfaces of MgB2 bulk samples produced by a pellet/closed tube method at two different sintering temperatures of 650 and 850 °C, after hot pressing at 200 °C, were irradiated with the same irradiation dose by using an ...