Effect of natural aging on RT and HSR superplasticity of ultrafine grained Zn-22Al alloy
Zn–22Al alloy was processed using a well-designed two-step equal channel angular extrusion/pressing (ECAE/P), and ultrafine-grained (UFG) microstructure with 200 nm grain size was achieved. UFG Zn-22Al was subjected to long-term (up to 60 days) aging at room temperature (RT) and it was seen that natural aging caused limited grain growth in the microstructure. Grain sizes of about 300 nm, 350 nm and 350 nm were measured after 15, 30 and 60 days aging, which mean that UFG Zn-22Al alloy has a good microstructural stability at RT up to 60 days. ECAPed Zn-22Al alloy showed a maximum elongation of about 400% at a high strain rate of 5×10-2 s-1 and maximum elongation decreased with increasing grain size. Elongation to failures of ~375% and ~350% were obtained with the samples having 300 nm and 350 nm grain sizes, respectively. In addition, natural aging slightly decreased the strain rate at which superplastic region formed. While the maximum elongation occurred at the strain rate of 5×10-2 s-1 in ECAPed UFG alloy, it took place at lower strain rate of 1×10-2 s-1 after aging for all time periods. Also, flow stress of the alloy increased with increasing grain size during natural aging. © 2016 Trans Tech Publications, Switzerland.
KaynakMaterials Science Forum
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
Achieving room temperature superplasticity in Zn-5Al alloy at high strain rates by equal-channel angular extrusion Multi-pass equal-channel angular extrusion/pressing (ECAE/P) was applied to the eutectic Zn-5Al alloy to achieve high strain-rate (HSR) superplasticity in that alloy at room temperature (RT) by producing ultrafine-grained ...
Effect of equal-channel angular pressing on room temperature superplasticity of quasi-single phase Zn-0.3Al alloy Quasi-single phase (dilute) Zn-0.3Al alloy was subjected to severe plastic deformation via equal-channel angular extrusion/pressing (ECAE/P), and the effects of ECAP on its room temperature (RT) and high strain rate (HSR) ...
High temperature superplasticity and deformation behavior of naturally aged Zn-Al alloys with different phase compositions Two Zn-Al alloys, eutectoid Zn-22Al and dilute Zn-0.3Al, were processed through equal-channel angular pressing (ECAP). The ECAP-processed alloys were subjected to long-term natural aging at room temperature for 120 days ...