Effect of equal-channel angular pressing on room temperature superplasticity of quasi-single phase Zn-0.3Al alloy
Üst veriTüm öğe kaydını göster
Quasi-single phase (dilute) Zn-0.3Al alloy was subjected to severe plastic deformation via equal-channel angular extrusion/pressing (ECAE/P), and the effects of ECAP on its room temperature (RT) and high strain rate (HSR) superplasticity and deformation mechanism were investigated. Multi-pass ECAP may refine the coarse-grained microstructure into the fine grained (FG) one. The grain size of Zn-matrix phase decreased down to 2.0m after ECAP. Many spherical Al-rich precipitates decomposed and homogeneously distributed inside the matrix phase. They are ultrafine grained (UFG) ?-particles with the grain sizes ranging from 50nm to ~200nm. This special microstructure having FG and UFG micro-constituents brought about an improvement in RT superplasticity even at HSRs. While multi-pass ECAP decreased flow stress of the alloy, its elongation to failure increased substantially depending on the initial strain rates. The maximum elongation was 1000% at a low strain rate of 10-4s-1, and 350% elongation was achieved at a high strain rate of 10-2s-1. Grain boundary sliding (GBS) was found to be the main deformation mechanism in region-II as the optimum superplastic region. © 2015 Elsevier B.V..
KaynakMaterials Science and Engineering A
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
High temperature superplasticity and deformation behavior of naturally aged Zn-Al alloys with different phase compositions Two Zn-Al alloys, eutectoid Zn-22Al and dilute Zn-0.3Al, were processed through equal-channel angular pressing (ECAP). The ECAP-processed alloys were subjected to long-term natural aging at room temperature for 120 days ...
Effect of different processes on lamellar-free ultrafine grain formation, room temperature superplasticity and fracture mode of Zn-22Al alloy The Zn-22 wt.%Al was processed using five different selected routes including thermal, thermo-mechanical and severe plastic deformation (SPD) techniques in order to produce ultrafine grained (UFG) microstructure for achieving ...
Room temperature superplasticity in fine/ultrafine-grained Zn-Al alloys with different phase compositions Three Zn-Al alloys, namely Zn-22Al, Zn-5Al and Zn-0.3Al, were subjected to equal-channel angular pressing (ECAP), and the effect of ECAP on their microstructure and room temperature (RT) superplastic behavior were investigated ...