GaN thin film deposition on glass and PET substrates by thermionic vacuum arc (TVA)
In this paper, GaN thin film production was realized by thermionic vacuum arc (TVA), a plasma deposition technique, for the first time. We present a new deposition mechanism for GaN thin films with a very short production time. Microstructure properties of samples were analyzed by X-ray diffractometry. The peak at 2? = 72.88° corresponding to GaN (0004) was detected in XRD spectra. The surface morphology of the deposited GaN films was analyzed using field emission scanning electron microscopy and atomic force microscopy. The surface properties of the produced samples are quite different. The average roughness values were determined to be 0.48 nm for GaN/PET and 1.17 nm for GaN/glass. The optical properties (i.e., refractive index and reflection) were determined using an interferometer. Moreover, the obtained optical data were compared with bulk GaN materials. The refractive indexes were measured as 2.2, 3,0 and 2,5 for the GaN/glass, GaN/PET and bulk GaN, respectively. The transparencies of the different GaN-coated substrates are nearly the same. The obtained band gap values were measured in the energy range of 3.3-3.5 eV. TVA is a novel non-reactive plasma technique for the generation of metal organic thin films. The main advantage of this method is its fast deposition rate without any loss in the quality of the films. © 2015 Elsevier B.V.
KaynakMaterials Chemistry and Physics
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
The influence of voltage applied between the electrodes on optical and morphological properties of the InGaN thin films grown by thermionic vacuum arc The aim of this research is to investigate the optical and morphological properties of the InGaN thin films deposited onto amorphous glass substrates in two separate experiments with two different voltages applied between ...
Optical and Surface Characteristics of Mg-Doped GaAs Nanocrystalline Thin Film Deposited by Thermionic Vacuum Arc Technique Magnesium (Mg) is the most promising p-type dopant for gallium arsenide (GaAs) semiconductor technology. Mg-doped GaAs nanocrystalline thin film has been deposited at room temperature by the thermionic vacuum arc technique, ...
In this paper, we introduced a new different thin film deposition method for heavily carbon doped GaAs. Used method is thermionic vacuum arc (TVA) and first used for the carbon doping process. The method is very fast ...