The role of cobalt doping on the optical and structural properties of Mn 3 O 4 nanostructured thin films obtained by SILAR technique
Özet
Cobalt doped manganese oxide thin films (Mn 3 O 4 :Co) were successfully deposited on soda lime glass substrates using SILAR technique. Mn 3 O 4 :Co thin films were characterized using XRD, SEM, Uv–VIS and Raman spectroscopy. The XRD spectra showed that thin films had substantially Hausmannite crystal structure. The preferential orientation of the pure and 0.5 at.% Co doped manganese oxide thin films (Mn 3 O 4 ) was (002), but with increasing Co doping, it was detected that this preferential orientation shift towards the (211) plane. The absorbance, transmittance and optical band gap of the Mn 3 O 4 :Co thin films were determined using Uv–Vis spectroscopy and these properties of the thin films differed considerably due to cobalt doping. The optical band gap of pure Mn 3 O 4 thin films was 2.00 eV, but on the other hand, due to the Co doping this value increased before and then decreased slightly. Optical transmittance of Mn 3 O 4 :Co films increased from 60% to 72% with the effect of Co doping. A1g mode, which is the characteristic vibration peak of Mn 3 O 4 films, was confirmed for pure and doped Mn 3 O 4 thin films at a wavelength of 658 nm. © 2019 Elsevier Ltd
Kaynak
Superlattices and MicrostructuresCilt
128Koleksiyonlar
İlgili Öğeler
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
-
Optical and surface properties of the in doped GaAs layer deposition using thermionic vacuum arc method
Pat S.; Özen S.; Şenay V.; Korkmaz Ş.; Şimşek V. (John Wiley and Sons Inc., 2016)A broadband optical transparent InGaAs semiconductor layer production of micron thicknesses was produced in only 75 s by thermionic vacuum arc (TVA) method at the first time. The optical and surface properties of the ... -
Optical and Surface Characteristics of Mg-Doped GaAs Nanocrystalline Thin Film Deposited by Thermionic Vacuum Arc Technique
Pat S.; Özen S.; Şenay V.; Korkmaz Ş. (Springer New York LLC, 2017)Magnesium (Mg) is the most promising p-type dopant for gallium arsenide (GaAs) semiconductor technology. Mg-doped GaAs nanocrystalline thin film has been deposited at room temperature by the thermionic vacuum arc technique, ... -
A study on some physical properties of a Pb-doped GaAs thin film produced by thermionic vacuum arc
Şenay V.; Özen S.; Pat S.; Korkmaz Ş. (Elsevier Ltd, 2017)A 155 nm Pb-doped GaAs thin film was deposited on a glass substrate by means of the thermionic vacuum arc technique in 30 s using GaAs and Pb pellets as source materials. Tools and techniques such as an optical reflectometer, ...