Yazar "Çolak M." seçeneğine göre listele
Listeleniyor 1 - 3 / 3
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Effect of copper addition to aluminium alloys on surface roughness in terms of turning operation(Polish Academy of Sciences, 2017) Özen F.; Fiçici F.; Dündar M.; Çolak M.Aluminium alloys have found usage in numerous industries due to some superior properties, such as high strength-to-weight ratios and high oxidation resistance. Aluminum alloys can be strengthened by some techniques. One of them, the most practical one, is precipitation hardening in aluminum alloys. By adding Cu, aluminum gains strength and hardness. In this work the machinability of unalloyed aluminum and aluminum alloyed with 4% and 8% of Cu have been investigated. Machinability assessment was executed in terms of surface roughness during turning operation. Specimens were manufactured by sand casting method, which is a commonly utilized casting operation. In machinability experiments, three different cutting tool materials were employed. Three different cutting speeds and three different feed rates have been used. Effect of these feeds, speeds and cutting tool materials on surface roughness has been studied. In addition, effect of Cu addition to aluminum alloys on surface roughness has been examined. © 2017, Polish Academy of Sciences. All rights reserved.Öğe Melt Cleanliness Comparison of Chlorine Fluxing and Ar Degassing of Secondary Al-4Cu(Springer Boston, 2016) Çolak M.; Kayikci R.; Dispinar D.The treatment of liquid aluminum prior to casting typically consists of purging gas and/or fluxes through the melt. By the use of several chemicals during these operations, several environmental problems can occur. Therefore, in this study, the melt cleanliness of Al-4Cu secondary alloy was investigated by comparing the use of argon degassing with or without chlorine fluxing. Reduced pressure test was used to assess the melt quality. Highest quality melt was obtained by Ar degassing with preheated graphite lance without the need to use any chemicals. © 2016, The Minerals, Metals & Materials Society and ASM International.Öğe Taguchi Approach for Optimization of Parameters that Effect Grain Size of Cast A357 Alloy(De Gruyter Open Ltd, 2017) Çolak M.; Dlşplnar D.Grain refining and modification are common foundry practice for improving properties of cast Al-Si alloys. In general, these types of treatments provide better fluidity, decreased porosity, higher yield strength and ductility. However, in practice, there are still some discrepancies on the reproducibility of the results from grain refining and effect of the refiner's additions. Several factors include the fading effect of grain refinement and modifiers, inhomogeneous dendritic structure and non-uniform eutectic modification. In this study, standard ALCAN test was used by considering Taguchi's experimental design techniques to evaluate grain refinement and modification efficiency. The effects of five casting parameters on the grain size have been investigated for A357 casting alloy. The results showed that the addition of the grain refiner was the most effective factor on the grain size. It was found that holding time, casting temperature, alloy type and modification with Sr were less effective over grain refinement. © by M. Çolak 2018.