Yazar "Guner S.B." seçeneğine göre listele

Listeleniyor 1 - 3 / 3
  • Küçük Resim Yok
    Öğe
    Comparison of Levitation Forces of Bulk MgB2 Superconductors Produced by Nano Boron and Carbon-Doped Nano Boron
    (Springer New York LLC, 2014) Duz I.; Guner S.B.; Erdem O.; Demir I.; Kapucu V.; Çelik Ş.; Ozturk K.; Hossain S.; Gencer A.; Yanmaz E.
    MgB2 bulk superconductors were prepared by hot press plus furnace heating method. Two types of boron powders were used, one is amorphous nano boron and the other is C-doped boron. Characteristics of superconductors were determined by XRD and resistance measurements. Systematic levitation force measurements were performed by using a modular system at low temperatures. These bulk superconductors showed around 9 N repulsive and 4 N attractive forces in the z-axis at 20 K at closest point to the cryostat lid which contains the MgB2 superconductor. These values slightly decreased by increasing temperature to 24 and 28 K for both samples. Comparing two samples, nano boron MgB2 showed slightly higher levitation force than C-doped MgB2 although C-doped MgB2 has higher attractive force value at the closest point. This situation points out that C-doped MgB2 is much proper for attractive force applications (as guidance force) while the nanoboron MgB2 sample is much appropriate for repulsive force (as levitation). © 2014, Springer Science+Business Media New York.
  • Küçük Resim Yok
    Öğe
    Effects of initial cooling conditions and measurement heights on the levitation performance of bulk MgB2 superconductor at different measurement temperatures
    (Springer New York LLC, 2014) Erdem O.; Ozturk K.; Guner S.B.; Celik S.; Yanmaz E.
    The levitation properties of MgB2 prepared by hot press at 200 ° C and then pellet/closed tube method has been investigated. The vertical and lateral levitation forces (Fz and Fx) on a cylindrical NdFeB permanent magnet (PM) below a disk-shaped bulk MgB2 were measured during the vertical and lateral traverses of the PM in different cooling heights (CHs) and measurement heights (MHs) at temperatures of 20, 25 and 30 K to investigate the effect of the initial CH and MH on the levitation performance of MgB2. For temperatures below 30 K, it was observed that Fz increases with increasing CH. However, a minute variation in Fz and a big hysteresis loop are observed at 30 K. From the lateral traverses, it was obtained that the Fz with attractive character increases with decreasing MH and the hysteresis effect increases for small MHs due to the increment of the magnetic field intensity which the sample feels with decreasing MH. In addition, it was seen that the character of Fx varies depending on both MH and measurement temperature. The higher hysteresis obtained in Fx than in Fz during lateral traverses implies that the motion of the flux lines in MgB2 is especially in lateral rather than vertical direction. Finally in this study, it was shown that the levitation performance of MgB2 depends not only on the measurement temperature but also on the CH and MH conditions. These results can be useful for optimizing the levitation performance of MgB2 superconductors for potential applications. © 2014 Springer Science+Business Media New York.
  • Küçük Resim Yok
    Öğe
    Improvement in levitation force performance of bulk MgB2 superconductors through coronene powder adding
    (Elsevier Ltd, 2017) Erdem O.; Abdioglu M.; Guner S.B.; Celik S.; Kucukomeroglu T.
    The effect of coronene (C24H12) addition on the levitation force properties of MgB2 superconductor has been investigated for the first time in this study. The polycrystalline disk-shaped MgB2 + y wt % C24H12 samples (y = 0, 2, 4, 6, 8, 10), were synthesized by a pellet/closed tube method at 850 °C under Ar atmosphere, after hot pressing at 200 °C. XRD analysis indicates a decrease in lattice parameters of coronene added samples and confirms substitution of carbon in boron sites. An increase in lattice strain and a decrease in grain size are observed due to the carbon substitution effect. Vertical and lateral levitation force measurements under zero-field-cooled and field-cooled regimes were carried out at different temperatures of 20, 25 and 30 K. It was found that the coronene addition significantly increases the high-field critical current density of MgB2. The Jc values were obtained as 4.6 × 103 Acm?2 and 1.3 × 104 Acm?2 for pure and 4 wt % coronene added samples at 20 K and 4 T. In addition, the levitation force measurements show that 4 wt % coronene adding is very effective in increasing both the vertical and lateral levitation force performances at 20 K. The maximum levitation force for 4 wt % coronene added sample corresponds to 7.58 N/g whereas the reference sample shows 6.73 N/g at 20 K in ZFC regime. The results point out that the hydrocarbon of C24H12 is an effective carbon-containing additive for MgB2 and can be useful for optimizing the levitation performance of MgB2 superconductors for potential applications. © 2017 Elsevier B.V.