PROCESSING OF GRADE A LOW CARBON STEEL BY EQUAL CHANNEL ANGULAR PRESSING
Küçük Resim Yok
Tarih
2020
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Nigde Omer Halisdemir University
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Grade A steel was processed using equal channel angular pressing (ECAP). 1 pass ECAP did not cause considerable decrease in the grain size of the steel. It brought about two different microstructures on flow and transverse planes of the ECAP billet, instead. Microstructure consists of elongated ferrite and perlite grains aligned in a direction having mainly 45° angle with the extrusion direction on the flow plane while nearly equiaxed grains were formed on the transverse plane. These differences between the microstructures of two different planes of the ECAP sample is attributed to the share planes that operative during ECAP. ECAP increased hardness and strength values of the steel significantly due to the increase in the dislocation density during the process. However, it decreased elongation to failure considerably. It was found that impact energy of the ECAP-processed sample is dependent on the notch position of the Charpy impact test sample
Açıklama
Anahtar Kelimeler
Material Production Technologies, Malzeme Üretim Teknolojileri
Kaynak
Nigde Omer Halisdemir University Journal of Engineering Sciences
Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi
Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi
WoS Q Değeri
Scopus Q Değeri
Cilt
9
Sayı
1