Effect of Fe Amount on Microstructure and Fluidity of A356 Alloy

Basit Öğe Kaydı
dc.authorid0000-0001-9550-6933
dc.contributor.authorDurmus, M.
dc.contributor.authorDispinar, D.
dc.contributor.authorGavgali, M.
dc.contributor.authorColak, M.
dc.date.accessioned2026-02-28T12:18:11Z
dc.date.available2026-02-28T12:18:11Z
dc.date.issued2025
dc.departmentBayburt Üniversitesi
dc.description.abstractThe most important factor affecting the production of quality parts with aluminum alloys is the quality of molten metal. One of the determining factors in molten metal quality is the minimization of trace impurity elements in the alloy. One of the most harmful impurities among these elements is Fe, and its amount is a determining factor in its negative effect. It is known that Fe negatively affects the quality of aluminum, causing a decrease in mechanical properties. Most of the Fe in the alloy forms intermetallic from needle-like to complex Chinese-script structures. In this study, carbon steel and stainless-steel rods were immersed in the liquid metal at casting temperatures of 700 degrees C and 750 degrees C in A356 aluminum casting alloy and were subjected to diffusion for 1, 2 and 5 hours. Subsequently, a 4-channel flow test mold with various section thicknesses was used. All samples were measured by measuring the liquid metal advance distances of all sections in mm. Then, microstructure analyses were performed on the obtained sections. As a result, it is observed that as Fe diffusion increases, liquid metal advancement distances decrease and Fe intermetallics form in the microstructure.
dc.identifier.doi10.24425/afe.2025.153797
dc.identifier.issn1897-3310
dc.identifier.issn2299-2944
dc.identifier.scopus2-s2.0-105016750697
dc.identifier.scopusqualityQ3
dc.identifier.urihttps://doi.org/10.24425/afe.2025.153797
dc.identifier.urihttps://hdl.handle.net/20.500.12403/6157
dc.identifier.wosWOS:001559385100001
dc.identifier.wosqualityQ4
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherPolska Akad Nauk, Polish Acad Sciences
dc.relation.ispartofArchives of Foundry Engineering
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_WoS_20260218
dc.subjectA356
dc.subjectFe content
dc.subjectIntermetallic
dc.subjectFluidity
dc.subjectFluidity index
dc.titleEffect of Fe Amount on Microstructure and Fluidity of A356 Alloy
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu