The Effect of Weathering on Color and Glossiness Properties of Polyurethane-Modified Water-Based Varnish Layers Applied to Thermally Treated Ash Wood
Küçük Resim Yok
Tarih
2025
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
North Carolina State Univ Dept Wood & Paper Sci
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
The effects of artificial weathering (168, 336, and 504 h) on the glossiness values and color parameters of varnished, polyurethane-modified ash wood were investigated. Samples included control samples without treatment and thermally treated samples under two different conditions (190 degrees C for 1.5 h and 212 degrees C for 2 h), all coated with a polyurethane-modified water-based varnish. In non-thermally treated and varnished samples, decreases in L* values were observed after weathering, while increases were noted in h(o), C*, b*, and glossiness at 60 degrees in both perpendicular and parallel directions to the fibers. After weathering, for samples thermally treated at 190 degrees C for 1.5 h and varnished, increases were observed in glossiness values at 20 degrees and 60 degrees in both directions, as well as in L*, b*, and h(o) values. Conversely, decreases were noted in a* and C* values. In samples thermally treated at 212 degrees C for 2 h and varnished, increases in a*, L*, h(o), b*, and C* values were detected after weathering, whereas decreases were observed in glossiness at all angles (20 degrees and 60 degrees) in both directions. The triangle E* values showed a decreasing trend in non-thermally treated varnished samples after weathering, while an increase was observed in samples thermally treated at 212 degrees C for 2 h and varnished.
Açıklama
Anahtar Kelimeler
Artificial weathering, Glossiness, Ash wood, Color, Water based varnish
Kaynak
Bioresources
WoS Q Değeri
Q2
Scopus Q Değeri
Q3
Cilt
20
Sayı
3